Recent Innovation in 3D and Tactile Effects in Plastics

by Ed Crutchley

Plastics Decoration Technology Watch

COURTESY/RH Solutions LLC

A screen printed RH UV WRINKLE


COURTESY/ECKART

A LUXAN effect pigment in plastic


Percentage repartition of patent applications to obtain 3D and tactile effects published during 2012.

Click Thumbnails to View

Patent applications cited and publication date:

  • 1. Ikonics. US20120237700A1 (Sep 20, 2012).
  • 2. Polyone. WO2011140381A2 (Nov 10, 2011).
  • 3. Dow global Technologies. WO2011155956A1 (Dec 15, 2011).
  • 4. Bader and Co. US20120133071A1 (May 21, 2012).
  • 5. KraussMaffei . WO2011154305A1 (Dec 15,2011).
  • 6. Plastipak Packaging . US8080295B2 (Dec 20, 2011).
  • 7. Nissei ASB. WO2012057090A1 (May 3, 2012).
  • 8. Clariant Masterbatches. WO2011137997A2 (Nov 10, 2011).
  • 9. Conopco. US8061541 (Nov 22, 2011).
  • 10. International Automotive Components Group. US8083979B2 (Dec 27, 2011).
  • 11. Daimler AG. US20120032592A1 (Feb 9, 2012).
  • 12. DIC. US20120006480A1 (Jan 12, 2012).
  • 13. LG Chem. WO2008147037 (Dec 4, 2008).
  • 14. SiPix Chemical. US20120003433A1 (Jan 5, 2012).
  • 15. Samsung Electronics. US20120001364A1 (Jan 5, 2012).
  • 16. Leonhard Kurz. US20120156445A1 (Jun 21, 2012).
  • 17. Nypro. WO2012112470A1 (Aug 23, 2012).
  • 18. 3M. WO2011081994A1 (Jul 7, 2011).
  • 19. Chiu. US20110117326A1 (May 19, 2011).
  • 20. Chiu. US2011209640A1 (Sep 1, 2011).
  • 21. Honda. US8101264B2 (Jan 24, 2012).
  • 22. Etansi. US20120196065A1 (Aug 2, 2012).
  • 23. Veriplast Decorative. US20110039046A1 (Feb 17, 2011).
  • 24. WO2012089827A1 (Jul 5, 2012).
  • 25. Multi-Color. US2011177267A9 (Jul 21, 2011).
  • 26. Theodore Hymmen. WO2011064075A2 (Jun 3, 2011).
  • 27. Süddekor. WO2011138441A1 (Nov 10, 2011).
  • 28. Tapematic. EP2407315A1 (Jan 18, 2012).
  • 29. Scodix. WO2011077200A1 (Jun 30, 2011).
  • 30. Scodix. WO2011110956A2 (Sep 15, 2011).
  • 31. Taica. US8123967B2 (Feb 28, 2012).
  • 32. DIC. US8252135B2 (Aug 28, 2012).
  • 33. KBS-Giori. US20110290129A1 (Dec 1, 2011).
  • 34. China Banknote SICPA. US20120055355A1 (Mar 8, 2012).
  • 35. Tai Ying Paint. CN101417277A (May 23rd, 2012).
  • 36. Leonhard Kurz. US8263191B2 (Sep 11, 2012).
  • 37. JDS Uniphase. EP2266710A2 (Dec 29, 2010).
  • 38. Kansai Paint. US8071170B2 (Dec 6, 2011).
  • 39. Duco. US20110154701A1 (Jun 30, 2011).
  • 40. PPE Holland. WO2011155819A3 (Dec 15, 2011).
  • 41. Minuta Technology. CN101282837B (Mar 21, 2012).
  • 42. Palo Alto Research Center. US20110115861A1 (May 19, 2011).
  • 43. Gillette. WO2011116036A2 (Sep 22, 2011).
  • 44. Sun Chemical. WO2012007563A3 ((Jul 19, 2012).
  • 45. 3D International Europe. US20120104637A1 (May 3, 2012).
  • 46. Travel Tags. US8056929 (Nov 15, 2011).
  •  

The most sought after features in plastics decoration either are a tactile surface feel or the visual impression of depth. These can be achieved by many methods, and new or evolving materials and processes for these are appearing almost every day. Often, attempts are made to protect new ideas by taking out intellectual property rights; trawling for new patent applications at the same time as watching out for general news items makes for a much improved method for keeping tabs on what is being thought of, where ideas are coming from and what we are likely to see marketed in the very near future.

The ultimate sought-after effect, of course, would be a tactile finish that can be regulated on the spot. The plastics decorating industry is starting to see the use of electrical or other physical impulses to alter the color, reflectivity or feel of a surface. For example, a notable recent discovery from Duke University is a polymer that changes from rough to smooth when a voltage is applied.

Many traditional solutions in this field continue to evolve, starting with molding. Inkjet, for example, has made it possible to print a resist onto a mold cavity surface prior to etching1. Where tactile effect has been achieved through choice of molded resin, complete or partial over-molding components with haptic materials has become increasingly common. A new continuously manufacturable super-soft TPE for over-molding2 is a plasticized styrene block copolymer (SBC) of Shore 000 hardness of between 45 and 60. A TPE has been developed for producing artificial leather skins for instrument panels3. Masterbatches that create haptic effects come from companies such as Kraiburg in Germany. Americhem of Cuyahoga Falls, OH, offers nGrain simulated wood-grain. Leather pellets also have been developed for adding as a masterbatch4.

In-mold coating or skinning is a relatively new way of applying such finishes. Engel and KraussMaffei5 in Germany have worked with companies such as Bayer MaterialScience and Evonik to develop in-mold coating of haptic finishes with their Dolphin and SkinForm processes respectively.

Blow molding is a highly versatile process that lends itself to being developed for special effects. One recent innovation is a process for a bottle on which the handle portion is coated with a tactile slip-resistant material of less than 60 Shore hardness6. A blow molded item can be subjected to a multistage blowing and reheating process in order to alter its shape and surface characteristics7. The extrusion rate of a viscous colored layer can be deliberately varied in order to create color swirls, waves, droplet-like elevations, crater-like cavities, and streaks of varying transparency in a bottle8. A blow molded bottle with a camouflage appearance9 recently has been seen – this process involves randomly extruding foaming material in order to create a 3D finish.

A depth look can be achieved by over-molding a layer of translucent polymer. This can be used to sandwich a decorative item such as a thin metal foil, film, fabric or digitally printed image or surface such as an imitation wood veneer, placed on a mold core, before sequentially injecting from behind and in front10. A light-transmitting rear layer can be used to illuminate the final object with integrated illumination11.

A recent invention calls for a process whereby a heat-shrinkable acrylic sheet is selectively reverse printed with IR-absorbing or -reflecting inks so that differential heat shrinkage occurs according to the printed pattern. The sheet then can be thermoformed onto a object to be decorated, thereby leaving a relief-patterned surface on the final part12.

In cases where special "effect" pigments are relied upon, new and more sophisticated types of pigment continue to appear from the likes of BASF, Eckart, JDSU, Merck, Silberline and many others. At least one or two of these appear every month.

In-mold decorative processes such as FIM, IMD, IMF, IML and IMR can be used to obtain tactile and 3D effects. DSM in Holland offers a license for in-mold tactile film application. One in-mold film offers visual cubic effect sheet with embedded glass beads backed by metallization13. The film can be optionally decorated.

3D patterns using in-mold film recently have been developed by several companies14-18. One example is a film that is 25-100 microns thick, and the 3D effect is screen printed with more than 70 microns thickness using epoxy ink with inorganic filler. The film is placed relief-side towards the polymer melt and is removed after molding19,20.

The film can be metallized and coated with a UV-cured 3D pattern21. A soft-feel film for IMR has been invented using 2-10 microns of compressible layer22. Raised areas in an in-mold label have been developed using MUCELL® technology23. The principle is to mold a polymer with an expansion agent and to selectively print areas of the inner side of the label with an ink that does not adhere to the melt.

When a separate decoration process is to be used, tactile effect UV screen printing inks come from the likes of Coates, Dubuit, Kiwo, Marabu, Nazdar and RH Solutions. Printers can use as few as 60x140-micron threads/inch to provide a Braille-like result. Inks and coatings also can be formulated to provide shrinkage phenomena during drying and curing in order to create crack and wrinkle effects. Surface tension phenomena can be used to create water droplet effects. Microcellular foaming of inks now can be induced by ultraviolet light.

Solvent and waterborne PU soft touch coatings are associated with well-known suppliers such as Bayer and Mankiewicz and have been around for years. Recently, these have been given improved chemical resistance24.

Laser etching can be used to selectively remove or roughen a surface.

A new shrink sleeve for closures includes a heat-activatable expandable layer in order to provide relief effects25.

Inkjet printing is another decoration process that lends itself to creating tactile finishes26,27. One recent development involves using an inkjet process for printing a relief surface on a component prior to metallizing, thereby creating an embossed effect referred to as ‘digital embossing’28. A decorative relief effect also has been obtained by inkjetting an adhesive and pouring a topping material, e.g. glitter, before curing and over-coating with an optional protective coating29.

A coil foil decoration process has been developed whereby the applied adhesive thickness applied to the substrate before foiling can be as much as 4 to 150 microns, thereby producing a relief metallic image once the foil has been transferred30.

Two well-known Japanese companies have developed water-transfer processes for imparting a tactile feel to a component31,32.

The idea of magnetically orientating pigments in order to obtain an apparent 3D effect has been around for decades, but it had only recently received significant attention, mostly for anti-counterfeit and security purposes. The principle is to bring an engraved magnet as close as possible (ideally <1mm) to a wet ink or coating in order to selectively orientate the pigment particles, and the effect can be impressive. Orientation can take a few seconds, so the ink or coating must be left ‘open’ during this time. The magnet can either be placed above or underneath the substrate, if substrate thickness allows. Various companies, particularly those in the security field, continue to develop improved magnetic orientation systems33,34,35,36,37.

Wet-on-wet coating effects have been produced using a double-basecoat finish followed by a partially-applied clear topcoat in order to achieve a patterned effect. The two coats only are partially miscible, thereby giving rise to a patterning effect38. Flow patterns have been produced on wet lacquer by selectively pouring an alcohol into areas of the wet coating39.

Lacquer surface texturing involves applying a lacquer to a substrate and then pressing a mold into the lacquer surface prior removing and curing40,41,42,43. Another method to create a 3D effect is to press a relief die into a hard topcoat covering a softer coating44. A recent invention involved selectively UV curing a coating and washing away uncured areas in order to create a lenticular effect. A light-steering variable thickness optical layer can produce a depth effect over printed moiré patterns45.

Methods to Obtain Tactile, Relief and 3D Effects in Plastics
Raw materials Resin TPE
Coloration Effect pigments
Wood grain, leather
Molding, in-mold Injection Engraved cavity
Film processes: FIM, IML, IMR
In-mold coating and skinning
Insert plus multi-shot
MUCELL/IML
Thermoforming Pre-printed IR absorbing/reflective pattern
Blow molding Heat re-forming
Tactile zones
Varied layer thickness
Zones of blowing agent
Decoration Inkjet Cracking inks
Foaming inks
Ink thickness variation
Screen Coarse screens
Cracking and wrinkling inks
Effect inks
High viscosity inks
Magnetically oriented pigments
Soft touch
Thick resists
Water droplet effect
Laser Selective etching
Cold foil Thick adhesive application
Water transfer Swelling or relief films
Coating (spray, roller, etc) Cracking and wrinkling coatings
Imprinting coating after curing
Imprinting lacquer before curing
Magnetically oriented pigments
Selective curing and washing away
Selectively pouring granular material over wet lacquer
Selectively pouring solvent over wet lacquer
Soft touch
Water droplet effects
Wet-on-wet application of immiscible products

Ed Crutchley is a specialist in plastics decoration and surface treatment. He provides a monthly innovation watch and annual survey for major players in the plastics industry. For more information, visit www.pdtechwatch.com.